ZC-SC125P 125℃ Self-crosslinking LSZH FR Polyolefin Material for Solar Cable

Categories Cable Material
Place of Origin: China
Brand Name: Zion communication OR OEM
Certification: CE,RoHS, VDE,UL,CUL,LPCB
Model Number: Solar cable
MOQ: 1,000 PCS
Packaging Details: Carton
Delivery Time: Normally 15 days
Payment Terms: T/T,L/C
Supply Ability: 10*20’GP/Month
Standard: EN50618-2014
Specifications: wires and cables up to 3KV.
Net weight: 25kg and B component is 5kg
Environment: clean, dry and ventilated warehouses
Warranty: 6 months
  • Haven't found right suppliers
  • Our buyer assistants can help you find the most suitable, 100% reliable suppliers from China.
  • And this service is free of charge.
  • we have buyer assistants who speak English, French, Spanish......and we are ready to help you anytime!
  • Submit Buying Request
    • Product Details
    • Company Profile

    ZC-SC125P 125℃ Self-crosslinking LSZH FR Polyolefin Material for Solar Cable

    125℃ Self-cross linking LSZH FRPolyolein Cable Compound
    ZC-SC125P
    General lnformation
    Description
    ZC-SC125P is a self-crosslinking low smoke zero halogen flame retardant polyolefin cable compound, which can be naturally cross-linked after being extruded into a cable. This product is mainly used for the sheath and insulation of photovoltaic cables that comply with TUV2Pfg-1169 and EN50618.
    Standard
    1) EN50618-2014
    2) 2Pfg1169/08-2007
    3) IEC60332-1-2-2015
    Specifications
    High temperature resistance XLPO Compound for wires and cables up to 3KV.
    Specification Sheet
    Product Properties
    UnitTest methodStandard
    Value
    Typical
    Value
    NationInternational
    Densityg/cm3GB/T 1033ISO 1183-11.40
    Tensile strengthMpaGB/T 1040.2ISO 527-2≥10.013.5
    Elongation at break%≥150250
    Air ageing
    (158±2℃,
    168h)
    Change of
    tensile strength
    %GB/T 2951.12IEC 60811-1±25+12
    Change of
    elongation
    %±25-8
    Volume resistivity (20℃)Ω·mGB/T 1410IEC 60093≥1.0x10122.6x1012
    Volume resistivity at operating temperature (125±2℃)Ω·m≥2.0x1083.5x108
    Dielectric strengthMV/mGB/T 1408.1IEC 60243-1≥2025
    Brittleness temperature (-40℃)℃)GB/T 5470ISO 974PassPass
    Hot set
    elongation
    (200℃,
    0.2Mpa,
    15min)
    Elongation
    under load
    %GB/T 2951.21IEC
    60811-2-1
    ≤10045
    Permanent
    deformation
    %≤250
    Water
    Immersion test
    (70℃, 168h)
    Change of
    tensile strength
    %GB/T 32129±30-3
    Change of
    elongation
    %±35-6
    Product Properties
    UnitTest methodStandard
    Value
    Typical
    Value
    NationInternational
    Oxygen index%GB/T 2406.2ISO 4589-2≥2835
    Smoke
    density
    non-luminous flameGB/T 8323.2ISO 5659-2≤350310
    flame combustion≤10070
    HCl and HBr content%GB/T 17650IEC 60754≤0.50
    HF content%≤0.10
    pH value≥4.35.0
    ConductivityμS/mm≤101.1
    NOTE: (1)The toxicity of smoke produced by materials shall be negotiated by both the supplier and the demander
    according to the needs of the product application.
    (2)Thetechnicalindicatorsspecifiedinthetablearethevaluesobtainedaftercrosslinking.
    Additional Information
    Processing Techniques:
    Extruding techniques
    It is recommended to use a low smoke zero halogen special screw, with a length to diameter ratio of L/D=20~25 and a compression ratio of 1.1~1.3. Because the actual temperature of the melt is related to the length diameter ratio, compression ratio and screw structure of the extruder, the appropriate extrusion temperature should be selected according to the specific situation of the extruder.
    The recommended setting temperatures for each zone of the extruder are as follows:
    ZoneZ1Z2Z3Z4HeadDie
    Temperature(℃)120130140140150150
    Using
    (1)When using this product, mix the A and B components evenly and drop them into the hopper.
    If color is required, the cable factory can use polyethylene base color masterbatch and materials
    within 8 hours after unpacking.
    (2)This product should not be shut down for a long time. If it is shut down for a long time, it is
    recommended to stop and clean the screw before starting up again.
    (3)To ensure sufficient crosslinking of the material, it is recommended that the cable be placed in
    a 70°C water bath or steam room for 6~8h, or at a constant temperature and humidity (23°C, 50%)
    for 7 days. The specific placement time is adjusted according to the thickness of the product and
    the crosslinking degree of the material, so as to meet the performance requirements of the cable.
    Package.Storage and Transport:
    PackageNet weightThe A and B component are kept in different bags, net weight of
    A component is 25kg and B component is 5kg
    MethodAluminum foil/polyethylene complex film bag for inner+ PP woven bag/
    PE/Kraft paper bag for outer
    TransportRequirementKeep away from the sunshine, rain and soaking during transport, as well
    as handle gently during carrying.
    StorageEnvironmentclean, dry and ventilated warehouses
    Warranty6 months

    Buy ZC-SC125P 125℃ Self-crosslinking LSZH FR Polyolefin Material for Solar Cable at wholesale prices
    Send your message to this supplier
     
    *From:
    *To: HANGZHOU ZION COMMUNICATION CO., LTD
    *Subject:
    *Message:
    Characters Remaining: (0/3000)
     
    Inquiry Cart 0