Building Material Self Levelling Cement Concrete For Vinyl Flooring 5 - 30 degrees centigrade M520
Note:
As the product contains cement, reacts with water to produce highly alkaline, avoid contact with skin, eyes; once contact, immediately flush with water; If skin or eye injury, seek immediate medical attention. This product will not produce the body, environmental impact material after hardening.
Packaging and Storage:
25kg composite bag. The product shall be kept indoors, pay attention to moisture, prevent freezing, exposure. Stacked on pallets no more than eight layers, the shelf life of six months.
Uses:
M520 standard using special self-leveling cement, fine aggregate and foreign brands of polymer spray powder resins and other raw materials such as cement additives, refined with a high mobility, self-leveling high plasticity of the foundation material for light commercial construction, family and other occasions.
Construction Method:
Primary Treatment:
Subfloor must be dry, solid, load-bearing, dust, debris hinder bonding, smooth surface. To ensure self-leveling surface strength and adhesion, water-based absorbent subfloor recommend using M318 primer. Stone, terrazzo base surface, tiles and other non-absorbent surface of the substrate, it is recommended to use M320 non-absorbent primer for processing.
Features:
Fast automatic leveling ground, fast-setting, low shrinkage
Construction can be freely controlled thickness
Construction thickness of 2-4mm, excellent compressive and flexural strength
Environmental protection
Technical Parameters:
Mixing ratio | 25kg cement : 6-6.5L water |
Theoretical application rate | 3kg/㎡.2mm |
Constructability time | about 20 minutes |
Viable human time | about 4 hours later |
The time of Laying the flooring | After the self-leveling is completely dried |
Compressive Strength | ≥22 MPa (after 28days) |
Flexural Strength | ≥4.0 MPa (after 28days) |