| Sign In | Join Free | My benadorassociates.com |
|
| Sign In | Join Free | My benadorassociates.com |
|
| Categories | Aluminum Oxide Ceramic |
|---|---|
| Brand Name: | KAMTAI |
| Model Number: | KTJC14-35 |
| Certification: | ISO 9001 |
| Place of Origin: | CHINA |
| MOQ: | 100PCS |
| Price: | Negotiable |
| Payment Terms: | L/C, T/T, Western Union, MoneyGram,PAYPAL |
| Supply Ability: | 20000PCS/ MONTH |
| Delivery Time: | 25 DAYS AFTER PAYMENT |
| Packaging Details: | CARTON BOX AND PLYWOOD PALLET |
| Name: | High temperature machinable Alumina ceramic bar with reliable quality and lower cost |
| Color: | White |
| Material: | 95% Alumina ceramic |
| Shape: | Rod |
Reliable Bar Shaped Alumina Ceramic Parts High Temperature Machinable
The alumina ceramic rod/bar is an ideal wear-resistance material for delivering the sand, mine, ash dregs and molten aluminium, has excellent conductivity, high machinery strength and high temperature resistance, can resist to the acid, high temperature, corrosion and static electricity. Al2O3 is the most important technical ceramic material. It is characterized by high hardness, high compressive strength and corrosion resistance even at high temperatures. Through the content of Al2O3 in the material,these properties can be tailored to the application of customer.
Features of alumina ceramic bar:
1.High temperature, Max working temperature: 1700C.
2.Excellent wear and abrasion resistance.
3.Good chemical corrosion resistance under high temperature.
4.High dielectric properties.
5. High oxidation resistance.
The specification of alumina ceramic bar:
| Unit | 95% Al2O3 | 99.7% Al2O3 | ZrO2 | |
| Color | - | white | ivory | white |
| Density | g/cm³ | 3.65 | 3.88 | 5.95 |
| Water Absorption | % | 0 | 0 | 0 |
| Young's Modulus | Gpa | 280 | 350 | 205 |
| Vickers Hardness | Gpa | 14 | 20 | 12 |
| Flexural Strength ( at R.T. ) | Mpa | 280 | 300 | 900 |
| Compressive Strength ( at R.T. ) | Mpa | 2000 | 2500 | 2200 |
| Thermal Conductivity ( at R.T. ) | W/(m.K) | 18-25 | 30 | 2.2 |
| Thermal Shock Resistance | ΔT(°C) | 220 | 180-200 | 280-350 |
| Max. Working Temperature ( at R.T. ) | °C | 1500 | 1700 | 850 |
| Volume Resistivity ( at R.T. ) | Ω.cm | >10^15 | >10^14 | >10^12 |
| Dielectric Constant (1 MHz at R.T. ) | - | 9.50 | 9.80 | 26 |
| Dielectric Strength | kV/mm | 16 | 22 | - |
|
High Acid Resistance Aluminum Oxide Ceramic Diaphragm With Smooth Surface
Durable Aluminum Oxide Ceramic Round Disk Plate Disc High Temperature High Precision
High Strength 95 % Aluminum Oxide Ceramic Bar High Precision Machining
Multi Corundum Cylinder Pole Aluminum Oxide Ceramic For Kiln , High Temperature Resistance
High Purity Insulating Thin 99% Alumina Ceramic Disc High Temperature Resistance
Customized High Pure Polished Aluminum Oxide Ceramic Bar Long Service Life
Square White Alumina Cermaic Plate High Heat Resistant Ceramic Plate
High Temperature Furnace Aluminum Oxide Ceramic Ceramic Heating Disc
Insulating Pink 95% Alumina Ceramic Sand Blasting Nozzle High Temperature Resistance
Biscuit Firing Tube Aluminum Oxide Ceramic In The Electroplating Industry