ISO Tensile 1100MPa 15CrNi6 1.5919 Forged Steel Bar

15CrNi6/1.5919 Quality Alloy Steel Black Bar

15CrNi6/1.5919 is a low-alloy steel containing chromium and Nickel as strengthening elements.It has good mechanical property for highly strained parts and good toughness at core tensile strength of 900 – 1200 N/mm². This materail is generally used driving bevel gears, crown wheels, gears, shafts, bolts for automotive and gear components.

Heat Treatment
Normalizing For 15CrNi6
1.Nominal normalizing temperature:850-880°C
2.Hold the temperature for several hours
3.Cooling in the air

Annealing For 15CrNi6
1.Nominal Annealing temperature:650-700°C
2.Cool slowly in the furance
3.Maximum Brinell hardness of 229

Hardening and Tempering(QT) For 15CrNi6
1.Nominal Hardening temperature:820-870°C
2.Hold at this temperature then quench in oil or water
3.Tempering as soon as possible when the temperature low to ambient
4.Heat uniformly to the suitable temperature.
5.keep the material out of the furnace ,then cool in the air

Mechanical Property( for reference only)
1.Tensile strength: 880-1100MPa
2.Yield point: 635MPa
3.Percentage reduction of area after fracture: 40%
4.Elongation after fracture: 11%
5.Impact test (+20°C): Longitud – 40~60J

Delivery Condition
1.Shape:Round/Square / Flat/Shafts/Rollers/Blocks
2.Surface condition:Black surface/Bright surface
3.Heat Treatment:Normalized/Annealed/QT
4.Straightness:Max 3mm/m(Enhanced straightness may be available on request)
5.Length:3000-5800mm suitable for 20″container. above 6000mm,suitable for 40″ container
6.Grain Size: 5-8 acc to ASTM E112-96
7.Ultrasonic Standard: Sep1921/ASTM A388/EN 10228-3
8.Non Metallic Inclusion: 2 max acc to ASTM E45 /K4≤20 acc to DIN 50602
9.Forging Ratio: minimum 4 : 1
10.Marking: Grade/Weight/Length/Size/Heat Number

Quality Certification
A material test report(Inspection Certificate EN 10204 3.1) will be provided, documenting the following:
1.Chemical analysis
2.Mechanical properties
3.Surface hardness
4.Non Metallic Inclusion
5.Heat Treatment Process
6.Grain size
7.Forging ratio
8.NDE test method/criteria

 We, Shanghai Unite Steel are committed to integrate engineering steel resources in china and serve the global engineering steel market. Our company has more than 15 years of experience in steel researching, production, managing and sales. And our team mostly are based on and worked in national famous steel enterprise.

In the aspect of resources and information, we have established cooperative and stronger relationship with nearly hundred enterprises, either state-owned or private owned in china, such as: DAYE Special Steel-a famous steel enterprise with the longest steelmaking history; BAO Steel, and Dongbei Special Steel Group-the biggest special steel manufacturer; TPCO, VALIN-largest seamless steel tube production enterprise; What's more, we have built long, deep and close business relationship with dozens of steel companies, Sharing and holding equities with several steel enterprises. Because of the close cooperation with steel companies and our pioneering spirit, which can ensure us stay at the top competition, and ensure our customers get what they really want!