| Categories | FeCrAl Alloy |
|---|---|
| Brand Name: | DLX |
| Model Number: | 0Cr21Al6 |
| Place of Origin: | China Jiangsu |
| MOQ: | 5 |
| Payment Terms: | L/C, T/T, Western Union, MoneyGram |
| Supply Ability: | 500 tons per month |
| Delivery Time: | 7-20 days |
| Packaging Details: | Spool package with Carton box, Coil package with polybag |
| Material: | Ferrous Chromium Aluminum |
| Resistivity: | 1.42+/-0.05 |
| Tensile Strength: | 630-780MPA |
| Elongtation: | ≥12% |
| Application: | Heating, Resistivity |
| Condition: | Hard / Soft |
| Sureface: | Bright, Oxided, Acide |
| Maximum Temperature: | 1250℃ |
| Melting Point: | 1500℃ |
| Name: | resistance heating flat wire |
| Certification: | CE,ROHS |
| Company Info. |
| Changzhou DLX Alloy Co., Ltd. |
| Verified Supplier |
| View Contact Details |
| Product List |
Iron-Chrome-Aluminum FeCrAl 0Cr21Al6 resistance heating alloy has high maximum service temperature in air up to 1250oC. Longer life permits large surface stress to be applied on the alloy. Lighter weight makes it a more economical resistance heating material than Nichrome. The electric resistivty remains almost constant with varying temperatures. Good yield strength and aging resistance. Outstanding form stability. Greater heat resistance than austenitic stainless steels therefore it is commonly used in the heating applications.
Infrared heaters, heating plates, irons, ceramic heaters & pots, fan heaters, quartz tube heaters, toasters, ovens, storage heaters, bead insulated coils, open coil components, hot air guns, convection heaters, radiators, industrial furnaces for heat processing, metal sheath tubular elements, suspended coil elements for air heaters
We manufacture resistance heating elements for the wide range of applications varying from industrial furnaces to domestic appliances.
Common Name: OhmAlloy142A
0Cr21Al6 Ferrous Chromium Aluminum FeCrAl resistance heating flat wire, ribbon.
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | |
 | ||
 | ||
 | ||
 | ||
 | ||
|
8mm Bright 830 MPA 0Cr27Al7Mo2 Resistance Wire FeCrAl Alloy
0.03mm 600 MPA 0Cr21Al4 Iron Chromium Aluminum Alloy
Bead Insulated Coils 0Cr25Al5FeCrAl 8mm Heating Wire FeCrAl Alloy
2.5mmx5mm Industrial Electric Furnace 0Cr21Al6Nb Strip FeCrAl Alloy
0Cr23Al5 fecral 0cr25al5 Wire 1300 Degree 630 MPA Oxidized Wire Ribbon Resistohm 135
Bright 0Cr27Al7Mo2 830 MPA 2.5mmx180mm FeCrAl Alloy
0Cr21Al6 Toasters 0.03mm Iron Chromium Aluminum Alloy
630 MPA FeCrAl Alloy
0Cr21Al4 High Chrome Iron
0.5x5mm FeCrAl Alloy