| Sign In | Join Free | My benadorassociates.com |
|
| Sign In | Join Free | My benadorassociates.com |
|
| Categories | Magnesia Chrome Brick |
|---|---|
| Brand Name: | CH Refractories |
| Model Number: | B322 B622 |
| Certification: | ISO |
| Place of Origin: | China |
| MOQ: | 1 Ton |
| Price: | USD 500-1000 per Ton |
| Payment Terms: | L/C, T/T |
| Supply Ability: | 5000 Ton per month |
| Delivery Time: | 5-15 working days |
| Packaging Details: | Pallet |
| name: | Magnesia Chrome Refractory |
| size: | 230*114*65mm |
| Application: | Industrial Furnaces, cement kiln |
| Bulk density: | 3.2-3.38 g/cm3 |
| Mgo content (%): | 45-60 or customized |
| Cr2O3 content (%): | 16-30 or customized |
| Company Info. |
| ZHENGZHOU CAIHUA KILN MASONRY INSTALLATION CO.,LTD |
| Verified Supplier |
| View Contact Details |
| Product List |
High Temperature Refractory Magnesia Chrome Refractory Used For Cement Rotary Kiln
Magnesia Chrome Refractory
The Magnesia Chrome Refractory brick is a product made of
high-purity magnesia and imported chrome concentrate, which is made
by adding a small amount of additives and high pressure and high
temperature. Generally there are three different magnesia chrome
refractory bricks according to manufacturing method, which are:
1.Common magnesite chrome refractory brick is made by sintered
magnesia and refractory level chrome ore as raw materials. The
space between refractory grains is bonded with silicate.
2.Direct-bonded magnesite chrome refractory brick is made by chrome
ore with low content of impurities and pure magnesite,firing at the
temperature above 1700°C.
3.Semi-rebonded and fuse-rebonded magnesite chrome refractory brick
are made by fused magnesite chrome sinter.
CH Refractories will suggest you the most suitable and economical magnesia chrome refractory brick according to your kiln or furnace casting condition to save your money and achieve the best performance.
| Items | CH-ZMGe | CH-ZMGe | CH-ZMGe | CH-ZMGe | CH-ZMGe | CH-ZMGe | ||||||
| / | 20A | 20B | 18A | 18B | 16A | 16B | 14A | 14B | 12A | 12B | 8A | 8B |
| Mgo% ≥ | 45 | 40 | 50 | 45 | 52 | 47 | 60 | 55 | 65 | 60 | 65 | 60 |
| Cr2O3% ≥ | 30 | 30 | 26 | 26 | 24 | 24 | 20 | 20 | 16 | 16 | 16 | 16 |
| Fe2O3% | 8-15 | 8-15 | 7-15 | 7-13 | 6-13 | 6-13 | 5-13 | 5-13 | 5-12 | 5-12 | 5-12 | 5-12 |
| SiO2% ≤ | 1.5 | 2.5 | 1.5 | 2.5 | 1.5 | 2.5 | 1.5 | 2.5 | 1.5 | 2.5 | 1.5 | 2.5 |
| Apparent porosity/% ≤ | 15 | 16 | 15 | 16 | 15 | 16 | 15 | 16 | 15 | 16 | 15 | 16 |
| Bulk density g/cm3 | 3.38 | 3.38 | 3.33 | 3.33 | 3.30 | 3.30 | 3.25 | 3.25 | 3.20 | 3.20 | 3.20 | |
Applications of Magnesite Chrome Brick:
Furnaces of metallurgy industry
Furnace of incineration of garbage
Furnaces of chemical industry and construction industry.
CFB (circulating fluidized bed) and heat treatment furnace
Packages of Magnesia Chrome Refractory
|
Corrosion Resistant Magnesite Chrome Brick Sintering With 7.5 Hardness
High Temperature MGO Furnace Chrome Bricks With Cold Crushing Strength And Refractoriness Of 1700 - 1800℃
1800 Degree Magnesia Chrome Brick With Good Thermal Shock Resistance
High Strength Magnesia Refractory Bricks Cold Crushing ≥50 MPa Hardness 7.5-8.5
MgO-Cr2O3 Magnesia Chrome Bricks With Linear Change ≤ 0.4% For Industrial
Nonferrous Metal Magnesia Chrome Brick Melting Sintered 1700C Refractory
B322 Nonferrous Metal Melting Sintered Magnesia Chrome Brick For Refining Furnace
Chrome Magnesite Bricks With Refractoriness 1700 - 1800℃ And Mohs Hardness 8.5
High Purity Magnesia CH Refractories Chrome Brick For Building Construction
Thermal Expansion Magnesite Chrome Mgo Brick 2.5-3.5×10-6/℃ Porosity ≤22%