| Categories | Water Based Acrylic Resin |
|---|---|
| Brand Name: | WeiLi Resin® |
| Model Number: | WQ-2015 |
| Certification: | ISO9001 |
| Place of Origin: | China |
| MOQ: | 5000KG |
| Price: | Negotiable |
| Payment Terms: | L/C, T/T |
| Supply Ability: | 500t/month |
| Delivery Time: | 14 work days |
| Packaging Details: | 200kg/drum |
| Appearance: | Milkywhite |
| Solid Content: | 50±1% |
| PH(25℃): | 8.0-9.0 |
| Acid Value: | 50 |
| Viscosity: | 1800-3000mPa*s |
| Tg: | -23℃ |
| Package: | 1000kg or 200kg |
| Company Info. |
| Xiamen WangQin Chemical Technology Co., Ltd. |
| Verified Supplier |
| View Contact Details |
| Product List |
Water Resistance Acrylic Emulsion Counterpart To Joncryl 624 For Flexo Plastic Varnish
Introduction
WQ-2015 acrylic emulsion has excellent water and rub resistance and film wetting and good ddhesion to lots of substrates. It is specially designed for flexo & gravure plastic inks and overprint varnishes. It promotes gloss, holdout, and resolubility in printing ink and overprint varnish formulations and can also be used to produce inorganic and organic pigment dispersion.
It is recommended to use WQ-2015 water based acrylic emulsion and WQ-2011 non-filming acrylic emulslion for water based flxography plastic varnish. The final inks will have excellent water resistance and rub resistance.
Physical Property:
| Appearance | Milky white |
| Solid Content (%) | 49±1 |
| Acid Value | 50 |
| Viscosity(mPa*s) | 1800-3000 |
| PH(25℃) | 8.0-9.0 |
| Tg(℃) | -23 |
| MFFT(℃) | <0 |
Rerefence Formulation For Water Based Varnish For Plastic Substrate (Flexography)
| No. | Raw Materials | % | |
| ① | WQ-2015 (film-forming) | 70.00 | |
| ② | WQ-2011 (non-film forming) | 19.00 | |
| ③ | WQ-2028 (improving gloss) | 5.50 | |
| ④ | Wax emulsion | 4.00 | |
| ⑤ | DOWSIL™ 51 : Ethanol (1:1) * | 1.00 | Dow Corning |
| ⑥ | Defoamer | 0.50 | TEGO Foamex 825 |
| Total | 100.00 | ||
| Remark: 1. ①＋②＋③+④+⑤＋⑥ Add the above materials and stir at the same time, at a constant speed, stirring time: about 30 minutes/300 rpm. 2. *: DOWSIL™ 51 Additive diluted with Ethanol =1:1 3. 4# cup: 25 seconds ± 2 PH value: 8.20 ± 0.5% 4. Final inks: varnish 70%+pigment paste 30% =100 (Ajusting it accoring to needs) | |||
Performance:
Storage
The product should be stored in a closed container to avoid freezing and high temperature. Suggested normal storage temperature is 10 to 35℃.
Packing
200kg small mouth plastic drum
Special Tips
This material is complied according to our existing technology and experience, the technical advice provided is sincere, but it is not guaranteed to be used in all samples and formulations, all the data are for users reference only.
|
High Gloss Water Based Acrylic Resin Solution For Printing Inks
Pigment Dispersion Water Based Acrylic Resin For Printing Ink
Soft Film Forming Acrylic Emulsion For Flexo And Gravure Ink And Varnish UV Primer
Acrylic Ammonia Solutions Acrylic Monoethanolamine Solutions For Color Concentrates
Water Based Acrylic Emulsion For Pre-Print Application
Low Molecular Weight Solid Styrene Acrylic Resin For High Gloss Overprint Varnish
Solid Styrene Acrylic Resin For Pigment Dispersions And Overprint Varnishes
Counterpart Of Induprint S103M Gloss Water Based Acrylic Resin Monoethanolamine Solution
Heat Resistant Acrylic Polymer For Pre Print And Post Print On Cardboard And Label
High Purity Transparent Waterborn Solid Acrylic Resin