| Categories | High Temperature Alloy |
|---|---|
| Brand Name: | CJ |
| Place of Origin: | China |
| MOQ: | 100kg. We also can accept sample order. |
| Payment Terms: | L/C, D/A, D/P, T/T, Western Union, MoneyGram |
| Supply Ability: | 10,000,000 tons/year |
| Delivery Time: | Fast delievery in7-10 days,up to order quantity |
| Packaging Details: | Industry standard packaging or according to client's requirement |
| name: | China Manufacturer High Quality Cold Rolled Steel Strip |
| Thickness: | 0.025mm-2.5mm or as required |
| Length: | As required |
| Technique: | Hot rolled |
| Surface: | 2B or according to customer requirement |
| Thickness tolerance: | ±0.01mm |
| Company Info. |
| Wuxi Chengjiu Metal Products Co., Ltd. |
| Verified Supplier |
| View Contact Details |
| Product List |
309s Cold Rolled Steel Strip 0.5mm Decorations High Temperature Applications
1. Introduction
The greatest difference between strip and sheet is the width of the coiled product. Any coiled product 24” and wider is considered sheet, while anything under 24” is described as strip. Today's precision slitters can produce widths as small as . 035”, but many applications below .
China Manufacturer High Quality Cold Rolled Steel Strip
Product Name stainless steel strip
| Material | Surface Treatment | Thickness | width |
| 201 | BA | 0.15-0.8mm | 10-800mm |
| 202 | BA | 0.15-0.8mm | 10-800mm |
| 304 | BA | 0.025-0.8mm | 10-800mm |
| 304 | CSP(1/2H,3/4H,H) | 0.08-1.0mm | 10-690mm |
| 301 | CSP(1/2H,3/4H,H,EH) | 0.08-1.0mm | 10-690mm |
| 309S | 2B | 0.08-2.0 | 10-690mm |
| 310S | 2B | 0.08-2.0 | 10-690mm |
| 430 | BA | 0.15-0.8mm | 10-800mm |
| 430 | 1D | 0.15-0.8mm | 10-690mm |
| 430 | 2D | 0.15-0.8mm | 10-690mm |
| 430 | H | 0.08-1.0mm | 10-690mm |
| 409 | HD | 0.15-0.8mm | 10-690mm |
2.Chemical composition and mechanical
200 series:
| level | Chemical composition | Mechanical properties | |||||||||||
| C | Si | Mn | P | S | Ni | Cr | N | Cu | Y.S | T.S. | ELOG. | HRB | |
| % | % | % | % | % | % | % | % | % | N/mm2 | N/mm2 | % | ||
| 201(1% Nickel) | ≤ 0.15 | ≤ 1.00 | 8~11 | ≤ 0.060 | ≤ 0.030 | 0.9~1.5 | 15~17 | ≤ 0.25 | 1.5~2 | ≥ 310 | ≥ 655 | ≥ 35 | ≤ 105 |
| 202(4% Nickel) | ≤ 0.15 | ≤ 1.00 | 6~9 | ≤ 0.060 | ≤ 0.030 | 3.5~5 | 15~17 | ≤ 0.25 | 1.5~2 | ≥ 260 | ≥ 620 | ≥ 40 | ≤ 100 |
300 series:
| level | Chemical composition | Mechanical properties | ||||||||||
| C | Si | Mn | P | S | Ni | Cr | Mo | Y.S | T.S. | ELOG. | HRB | |
| % | % | % | % | % | % | % | % | N/mm2 | N/mm2 | % | ||
| 304 | ≤ 0.08 | ≤ 0.75 | ≤ 2 | ≤ 0.045 | ≤ 0.03 | 8~10 | 18~20 | ≥ 205 | ≥ 520 | ≥ 40 | ≤ 90 | |
| 301 | ≤ 0.15 | ≤ 1.00 | ≤ 2 | ≤ 0.045 | ≤ 0.03 | 6~8 | 16~18 | ≥ 205 | ≥ 515 | ≥ 40 | ≤ 95 | |
| 316 | ≤ 0.08 | ≤ 1.00 | ≤ 2 | ≤ 0.045 | ≤ 0.03 | 10~14 | 16~18 | 2~3 | ≥ 205 | ≥ 515 | ≥ 40 | ≤ 90 |
| 316L | ≤ 0.03 | ≤ 1.00 | ≤ 2 | ≤ 0.045 | ≤ 0.03 | 12~15 | 16~18 | 2~3 | ≥ 170 | ≥ 480 | ≥ 40 | ≤ 95 |
400 series:
| level | Chemical composition | Mechanical properties | |||||||||||
| C | Si | Mn | P | S | Ni | Cr | N | Cu | Y.S | T.S. | ELOG. | HRB | |
| % | % | % | % | % | % | % | % | % | N/mm2 | N/mm2 | % | ||
| 430 | ≤ 0.12 | ≤ 1.00 | ≤ 1 | ≤ 0.040 | ≤ 0.030 | 16~18 | ≥ 450 | ≥ 205 | ≥ 22 | ≤ 88 | |||
3.Product Show
|
Nickel-Chromium-Iron High Temperature Steel 8.2g/cm3 Density
Heat Resistant Steel with Excellent Corrosion Resistance Good Weldability and Melting Point of 1400-1450℃
High Yield Strength Nickel-Chromium-Iron Alloy for High Temperature Performance
High Temperature Alloy with Excellent Corrosion Resistance and Good Weldability
High Quality Thermal Expansion 11.2×10-6/K Steel with Good Weldability and Excellent Corrosion Resistance
High Formability 400MPa Yield Strength Alloy
Excellent Oxidation Resistance 11.2×10-6/K High Temperature Alloy
High Tensile Strength 550MPa Alloy with Good Weldability and 8.2g/cm3 Density
High Tensile Strength 550MPa Alloy with Excellent Oxidation Resistance
High Performance Heat Resistant Alloy with Good Machinability and Melting Point 1400-1450℃