| Brand Name: | BAOSTEEL TISCO |
| Model Number: | 201 202 301 304 316L 321 309S 310S 317L 329 347 2205 .etc |
| Certification: | ISO |
| Place of Origin: | China |
| MOQ: | 1 Ton |
| Price: | 1200 -2000 USD/Ton |
| Payment Terms: | L/C, T/T, Western Union |
| Supply Ability: | 20Ton per week |
| Delivery Time: | 5 - 12 days based on the quantity |
| Packaging Details: | standard packing for export |
| Products: | Stainless Steel Sheet |
| Grade: | 200 series 300 series 400 series |
| Thickness: | 0.3 - 3.0mm |
| Tech: | cold rolled |
| Width: | 1000mm 1219mm 1500mm or customs as request |
| Surface: | 2B BA NO.1 NO.4 8K HL Color finishing |
| Standard: | ASTM GB JIS EN DIN |
| MOQ: | 1 Ton |
| Company Info. |
| JIANGSU MITTEL STEEL INDUSTRIAL LIMITED |
| Verified Supplier |
| View Contact Details |
| Product List |
TISCO 445 Stainless Steel Sheet JIS G4305 Thickness 0.6 - 2.0mm Cold Rolled 2B
Stainless steel grade 445 is one of the most widely used precipitation hardening grade steels. Although this material is soft and ductile in the solution annealed condition, it is very capable of good properties with a single precipitation or aging treatment. This steel possesses good corrosion resistance, high harness, toughness and strength.
The following datasheet provides an overview of stainless steel grade 445.
The chemical composition of grade 445 stainless steel is outlined in the following table.
| Element | Content (%) |
|---|---|
| Iron, Fe | Balance |
| Chromium, Cr | 19-21 |
| Silicon, Si | ≤1.00 |
| Manganese, Mn | ≤1.00 |
| Nickel, Ni | ≤0.60 |
| Phosphorous, P | ≤0.04 |
| Carbon, C | ≤0.020 |
| Sulfur, S | ≤0.012 |
The mechanical properties of grade 445 stainless steel are displayed in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 427 MPa | 61931 psi |
| Yield strength | 205 MPa | 29732 psi |
| Modulus of elasticity | 190-210 GPa | 27557- 30457 ksi |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break | 22% | 22% |
| Hardness | 83 | 83 |
The 445 stainless steel grade can be machined into long gummy chips. For heat treatment of this material, it must be soaked at 1038°C (1900°F) for 30 min and then cooled below 16°C (60°F) for complete martensite transformation. Common fusion and resistance methods can be used to weld grade 445 steel. Oxyacetylene welding should be avoided. AWS E/ER630 filler metal is recommended. The material has to be soaked for 1 h at 1177°C (2150°F) for performing forging. The material should not be worked below 1010°C (1850°F). Before final hardening, post-work solution treatment is required.
Applications
White goods: Dish washer and dryers, refrigerator business use, microwave ovens, washing machine tubs,
induction heaters, rice cookers
Automotive Exhaust system: Catalytic converter
Kitchenware: Cookware
We stock AISI 445, JIS SUS445J1, SUS445J2 hot and cold rolled steel sheet, plate, strip and coil.
|
439 Stainless Steel Sheet 2B 2D Finishing 0.8-3.0mm TISCO POSCO
443 ASTM DIN GB Standard 0.4-3mm Stainless Sheet Cold Rolled
0.4-100mm 317L Stainless Steel Sheet 1000mm EN 1.4438 UNS S31703 EN 10088-2
Heat Resistant Stainless Steel Plate EN 1.4833 X12CrNi23-13 3.0-30.0mm
EN 1.4571 Hot Rolled Stainless Steel Sheet 1500mm 2000mm EN 10088-2 X6CrNiMoTi17-12-2
EN 1.4841 0.6-30.0mm AISI 314 Stainless Steel Metal Plate
Duplex 1.4462 3 Mm Stainless Steel Sheet EN 10088-2 Hot Rolled Duplex
EN 1.4319 EN ASTM JIS 301 Stainless Steel Plate 0.4-30mm
Gold Etching 304 201 Stainless Steel Sheet Gold Color ASTM EN DIN JIS GB
0.3-2.0mm 201 304 Black Mirror Stainless Steel Decorative Sheets