| Categories | FeCrAl Alloy |
|---|---|
| Brand Name: | DLX |
| Model Number: | 0Cr21Al6Nb |
| Place of Origin: | China Jiangsu |
| MOQ: | 5 |
| Payment Terms: | L/C, T/T, Western Union, MoneyGram |
| Supply Ability: | 500 tons per month |
| Delivery Time: | 7-20 days |
| Packaging Details: | Spool package with Carton box, Coil package with polybag |
| Material: | Ferrous Chromium Aluminum |
| Resistivity: | 1.45+/-0.05 |
| Tensile Strength: | 630-780MPA |
| Elongtation: | ≥12% |
| Application: | Heating, Resistivity |
| Condition: | Hard / Soft |
| Sureface: | Bright, Oxided, Acide |
| Maximum Temperature: | 1350℃ |
| Melting Point: | 1510℃ |
| Name: | resistance heating wire |
| Certification: | CE,ROHS |
| Company Info. |
| Changzhou DLX Alloy Co., Ltd. |
| Verified Supplier |
| View Contact Details |
| Product List |
0Cr21Al6Nb alloy has the characteristic of high resistivity, low temperature resistance coefficient, high operating temperature, good anti-oxidation and anti-corrosion under high temperature.
In industrial heating applications, 0Cr21Al6Nb resistance wire is widely used in various heating equipment due to its high-temperature resistance, oxidation resistance, and stable resistance characteristics, providing reliable heating solutions for industrial production.
0Cr21Al6Nb resistance wire is commonly used to manufacture industrial heating tubes and heating plates for heating various fluid mediums, such as water, oil, gases, as well as solid objects. These heating devices find extensive applications in heating processes in fields such as chemical, pharmaceutical, and food processing industries.
In industrial heating, heat guns and hot air furnaces are used to provide high-temperature air or airflow for processes such as drying, baking, melting, etc. 0Cr21Al6Nb resistance wire is installed as heating elements in these devices, generating heat when electric current passes through, heating the air or airflow to the desired temperature.
In metal smelting and materials processing, melting furnaces and sintering furnaces are used to heat and process metals, alloys, and ceramic materials. 0Cr21Al6Nb resistance wire is applied as heating elements in these furnaces, providing the required high-temperature environment to achieve processes such as metal melting, alloy blending, ceramic sintering, etc.
In addition to the mentioned equipment, 0Cr21Al6Nb resistance wire is also applied in various other industrial heating equipment such as heat treatment furnaces, vacuum furnaces, injection molding machine heaters, etc., to provide stable heating sources.
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | |
 | ||
 | ||
 | ||
 | ||
 | ||
|
8mm Bright 830 MPA 0Cr27Al7Mo2 Resistance Wire FeCrAl Alloy
0.03mm 600 MPA 0Cr21Al4 Iron Chromium Aluminum Alloy
Bead Insulated Coils 0Cr25Al5FeCrAl 8mm Heating Wire FeCrAl Alloy
2.5mmx5mm Industrial Electric Furnace 0Cr21Al6Nb Strip FeCrAl Alloy
0Cr23Al5 fecral 0cr25al5 Wire 1300 Degree 630 MPA Oxidized Wire Ribbon Resistohm 135
Bright 0Cr27Al7Mo2 830 MPA 2.5mmx180mm FeCrAl Alloy
0Cr21Al6 Toasters 0.03mm Iron Chromium Aluminum Alloy
630 MPA FeCrAl Alloy
0Cr21Al4 High Chrome Iron
0.5x5mm FeCrAl Alloy