| Brand Name: | FEIHONG TOPO |
| Model Number: | T-RAL1000 |
| Certification: | CE, BV, ROHS |
| Place of Origin: | China |
| MOQ: | Negotiable |
| Price: | Negotiable |
| Payment Terms: | L/C, T/T, Western Union, MoneyGram |
| Supply Ability: | 400 T/Month |
| Delivery Time: | 7 days |
| Packaging Details: | Two-ply PVC bag inside with carton box, net weight 20/25kg |
| Color: | Green beige |
| Application Method: | Spray |
| Feature: | Green |
| Surface Type: | outdoor metal furniture |
| Package: | 20kg |
| Materials: | Epoxy |
Hammered textured Powder Coat Motorbike Frame Powder Coating Epoxy Materials RAL 1000 Color
Epoxy based powder coating that exhibits excellent corrosion protection and chemical resistance when applied over a properly prepared metal substrate. Designed for interior application only.
Pack Size | 25 kg (55.1 lb) |
Color | Green beige |
Gloss | Low 0 - 20 |
Finish | Texture |
Special Finishes | Texture |
Environment | Interior |
Chemistry | Epoxy |
Gloss at 60 Degrees | 3-10 |
Specific Gravity | 1.4 |
Impact Resistance (in/lb) | 80 |
Cure Schedule (Degrees F/mins) | 400F/5 min |
Former Product Code | 11-7001 |
Recommended Film Thickness (mils) | 2.1-3.2 |
Inspection Item | Test Standard or Method | Test Indicator | |||
| Type A | Type B,C | ||||
| Impact resistance | ISO6272 | GB/T1732-1993 | 40cm | 50cm | |
| Cupping test | ISO1520 | GB/T9753-1988 | 5mm | 8mm | |
| Adhesion(Planning grid method) | ISO2409 | GB/T9286-1998 | Grade 0 | ||
| Crook | ISO1519 | GB/T6742-1986 | 3mm | 2mm | |
| Pencil hardness | ASTMD3363 | GB/T6739-1996 | 1H-2H | ||
| Salt test | ISO7253 | GB/T1771-1991 | > 500 hours | ||
| Heat test | ISO6270 | GB/T1740-1979 | > 1000 hours | ||
| Heat resistance | 100°C/24 hours (white) | Paul Light character (best) | |||
Remark | 1, Cold-rolled steel to remove rust,oil for testing, film thickness: 50-70um. 2, All the indicators of film features will be down lightly depending on reducing of luster | ||||




|