| Material: | 95% Alumina Ceramics |
| Color: | White |
| Density: | 3.6 g/cm³ |
| Maximum Use Temperature: | 1600 ℃ |
| OEM,ODM: | Acceptable |
| Orgin: | WUXI JIANGSU CHINA |
| MOQ: | 100 PCS |
| Package: | Carton |
| Company Info. |
| Yixing Hengyuan Ceramic Technology Co., Ltd. |
| Verified Supplier |
| View Contact Details |
| Product List |
Alumina ceramic(Al2O3), is an industrial ceramic that has high hardness, is long wearing, and can only be formed by diamond grinding.Because of its great performance,alumina ceramic is widely used in many fields.can meet the requirement of daily using and specifical features.
Features Of Alumina Ceramic :
1. Shape : customizable
2. Colour : white
3. High thermal conductivity
4. Good corrosion resistance
| Naterial | Unit | A95% Alumina Ceramics | A97% Alumina Ceramics | A99% Alumina Ceramics | A99.7% Alumina Ceramics |
| Density | g/cm³ | 3.6 | 3.72 | 3.85 | 3.85 |
| Flexural Strength | Mpa | 290 | 300 | 350 | 350 |
| Compressive Strength | Mpa | 3300 | 3400 | 3600 | 3600 |
| Modulus of Elasticity | Gpa | 340 | 350 | 380 | 380 |
| Impact Resistance | MPam1/2 | 3.9 | 4 | 5 | 5 |
| Weibull Modulus | M | 10 | 10 | 11 | 11 |
| Vickers Hardulus | HV0.5 | 1800 | 1850 | 1900 | 1900 |
| Thermal Expansion Coefficient | 10-6K-1 | 5.0-8.3 | 5.0-8.3 | 5.4-8.3 | 5.4-8.3 |
| Thermal Conductivity | W/Mk | 23 | 24 | 27 | 27 |
| Thermal Shock Resistance | △T℃ | 250 | 250 | 270 | 270 |
| *Maximum Use Temperature | ℃ | 1600 | 1600 | 1650 | 1650 |
| Volume Resistivity at 20℃ | Ω | ≥1014 | ≥1014 | ≥1014 | ≥1014 |
| Dielectric Strength | KV/mm | 20 | 20 | 25 | 25 |
| Dielectric constant | εr | 10 | 10 | 10 | 10 |

















|