| Categories | FeCrAl Alloy |
|---|---|
| Brand Name: | DLX |
| Model Number: | 0Cr27Al7Mo2 |
| Place of Origin: | China Jiangsu |
| MOQ: | 5 |
| Price: | Negotiable |
| Payment Terms: | L/C, T/T, Western Union, MoneyGram |
| Supply Ability: | 500 tons per month |
| Delivery Time: | 7-20 days |
| Packaging Details: | Spool package with Carton box, Coil package with polybag |
| Material: | Ferrous Chromium Aluminum |
| Resistivity: | 1.53+/-0.05 |
| Tensile Strength: | 680-830MPA |
| Elongtation: | ≥10% |
| Application: | Heating, Resistivity |
| Condition: | Hard / Soft |
| Sureface: | Bright, Oxided, Acide |
| Maximum Temperature: | 1400℃ |
| Melting Point: | 1520℃ |
| Name: | FeCrAl resistance heating wire |
| Certification: | CE,ROHS |
| Company Info. |
| Changzhou DLX Alloy Co., Ltd. |
| Verified Supplier |
| View Contact Details |
| Product List |
0Cr27Al7Mo2 is an iron-chromium-aluminium alloy (FeCrAl alloy) for use at temperatures up to 1400°C (2552°F). The alloy with the characteristics of high resistivity, low temperature coefficient of electric resistance, high operating temperature, good oxidation resistance under high temperature. It can equal to APM.
In heat treatment equipment, 0Cr27Al7Mo2 resistance wire is commonly used as a heating element to provide the required heating power. By passing current through the resistance wire, it generates heat that is transferred to the workpiece, facilitating the heating stage of the heat treatment process. Due to its high temperature resistance and excellent oxidation resistance, 0Cr27Al7Mo2 resistance wire can operate stably at high temperatures, ensuring the heat treatment equipment provides consistent heating effects.
With its good thermal conductivity, 0Cr27Al7Mo2 resistance wire can evenly transfer heat to the surface of the workpiece, ensuring temperature uniformity during the heat treatment process. This is crucial for heat treatment processes that require precise temperature control to ensure consistent treatment effects on the workpiece.
In some specialized heat treatment processes, corrosive gases or chemicals may be present, placing higher demands on the corrosion resistance of heating elements. Due to its excellent oxidation resistance and corrosion resistance, 0Cr27Al7Mo2 resistance wire can operate stably in such environments, maintaining long-term stable heating performance.
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | |
 | ||
 | ||
 | ||
 | ||
 | ||
|
8mm Bright 830 MPA 0Cr27Al7Mo2 Resistance Wire FeCrAl Alloy
0.03mm 600 MPA 0Cr21Al4 Iron Chromium Aluminum Alloy
Bead Insulated Coils 0Cr25Al5FeCrAl 8mm Heating Wire FeCrAl Alloy
2.5mmx5mm Industrial Electric Furnace 0Cr21Al6Nb Strip FeCrAl Alloy
0Cr23Al5 fecral 0cr25al5 Wire 1300 Degree 630 MPA Oxidized Wire Ribbon Resistohm 135
Bright 0Cr27Al7Mo2 830 MPA 2.5mmx180mm FeCrAl Alloy
0Cr21Al6 Toasters 0.03mm Iron Chromium Aluminum Alloy
630 MPA FeCrAl Alloy
0Cr21Al4 High Chrome Iron
0.5x5mm FeCrAl Alloy