| Sign In | Join Free | My benadorassociates.com |
|
| Sign In | Join Free | My benadorassociates.com |
|
| Categories | FeCrAl Alloy |
|---|---|
| Brand Name: | DLX |
| Model Number: | 0Cr27Al7Mo2 |
| Place of Origin: | China Jiangsu |
| MOQ: | 5 |
| Price: | Negotiable |
| Payment Terms: | L/C, T/T, Western Union, MoneyGram |
| Supply Ability: | 500 tons per month |
| Delivery Time: | 7-20 days |
| Packaging Details: | Spool package with Carton box, Coil package with polybag |
| Material: | Ferrous Chromium Aluminum |
| Resistivity: | 1.53+/-0.05 |
| Tensile Strength: | 680-830MPA |
| Elongtation: | ≥10% |
| Application: | Heating, Resistivity |
| Condition: | Hard / Soft |
| Sureface: | Bright, Oxided, Acide |
| Maximum Temperature: | 1400℃ |
| Melting Point: | 1520℃ |
| Name: | FeCrAl resistance heating wire |
| Certification: | CE,ROHS |
| Company Info. |
| Changzhou DLX Alloy Co., Ltd. |
| Verified Supplier |
| View Contact Details |
| Product List |
0Cr27Al7Mo2 is an iron-chromium-aluminium alloy (FeCrAl alloy) for use at temperatures up to 1400°C (2552°F). The alloy with the characteristics of high resistivity, low temperature coefficient of electric resistance, high operating temperature, good oxidation resistance under high temperature. It can equal to APM.
0Cr27Al7Mo2 resistance wire is commonly used in electric heaters such as electric kettles, water dispensers, and electric pots. They use the heat generated by the resistance wire to heat water to the desired temperature, providing hot water and beverages for daily household needs.
In ovens and microwaves, 0Cr27Al7Mo2 resistance wire serves as a heating element, responsible for heating food to the desired temperature. They can quickly and evenly transfer heat to the food, ensuring effective heating and better cooking results.
Electric blankets and heating pads use the heat generated by 0Cr27Al7Mo2 resistance wire to provide users with a warm and comfortable sleeping environment. They can evenly heat the bed surface, alleviate discomfort from cold weather, and improve sleep quality.
In hair dryers and electric irons, 0Cr27Al7Mo2 resistance wire is used as a heating element to accelerate airflow or provide heat, facilitating quick hair drying or clothes ironing.
Water heaters and boilers commonly use 0Cr27Al7Mo2 resistance wire as a heating element to heat cold water to the desired temperature, providing hot water supply for bathing and cleaning needs.
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | |
 | ||
 | ||
 | ||
 | ||
 | ||
|
8mm Bright 830 MPA 0Cr27Al7Mo2 Resistance Wire FeCrAl Alloy
0.03mm 600 MPA 0Cr21Al4 Iron Chromium Aluminum Alloy
Bead Insulated Coils 0Cr25Al5FeCrAl 8mm Heating Wire FeCrAl Alloy
2.5mmx5mm Industrial Electric Furnace 0Cr21Al6Nb Strip FeCrAl Alloy
0Cr23Al5 fecral 0cr25al5 Wire 1300 Degree 630 MPA Oxidized Wire Ribbon Resistohm 135
Bright 0Cr27Al7Mo2 830 MPA 2.5mmx180mm FeCrAl Alloy
0Cr21Al6 Toasters 0.03mm Iron Chromium Aluminum Alloy
630 MPA FeCrAl Alloy
0Cr21Al4 High Chrome Iron
0.5x5mm FeCrAl Alloy