Alloy 200 Seamless Pipes UNS N02200/W.Nr. 2.4060 Nickel 200 Pipe Tubes for Aerospace

Alloy 200 Seamless Pipes UNS N02200/W.Nr. 2.4060 Nickel 200 Pipe Tubes for Aerospace

Nickel 200 Pipe Tubes UNS N02200 Seamless Pipes Alloy 200

• Nickel (Ni): 99.0 min
• Copper (Cu): 0.25 max
• Iron (Fe): 0.40 max
• Manganese (Mn): 0.35 max
• Carbon (C): 0.15 max
• Silicon (Si): 0.35 max
• Sulfur (S): 0.01 max

• High Purity Nickel: Composed of at least 99.0% nickel, Nickel 200 offers excellent resistance to a wide range of corrosive media.
• Corrosion Resistance: Outstanding resistance to caustic alkalis, particularly sodium hydroxide, even at high temperatures. Also resistant to neutral and alkaline salt solutions.
• Thermal Conductivity: High thermal conductivity makes it suitable for heat exchangers and other thermal transfer applications.
• Magnetostrictive Properties: Nickel 200 has notable magnetostrictive properties, making it useful in various electronic and electromagnetic applications.
• Mechanical Properties: Good mechanical properties over a wide range of temperatures and conditions.

• Chemical Processing: Equipment and piping in chemical processing plants due to its resistance to various chemicals.
• Food Processing: Used in equipment for food production due to its resistance to many organic and inorganic compounds.
• Marine and Offshore: Components exposed to corrosive seawater environments.
• Electronics: Electrical and electronic components due to its excellent electrical conductivity.
• Aerospace: Used in aerospace applications for its strength and resistance to various corrosive environments.

• ASTM B161 / ASME SB161
• ASTM B163 / ASME SB163
• ASTM B725 / ASME SB725

• Tensile Strength: 67 ksi (462 MPa) min
• Yield Strength (0.2% offset): 21 ksi (145 MPa) min
• Elongation: 40% min
• Hardness: Approximately 70 HRB (Rockwell B Hardness)

• Seamless Pipes/Tubes: Manufactured by extrusion, rotary piercing, or other similar processes to ensure a high-quality product with no weld seams.
• Welded Pipes/Tubes: Produced by forming and welding the material, followed by heat treatment to ensure the desired properties.

• Outer Diameter (OD): Typically ranges from 0.5 inches to 8 inches.
• Wall Thickness: Available in schedules ranging from SCH 5S to SCH XXS, depending on the application requirements.

• Pipes and tubes can be supplied with various surface finishes, including pickled, polished, or with a specific roughness as required by the application. Other finishes like bright annealed or ground finishes can also be provided.

• Nickel 200 can be annealed to restore ductility after cold working and to achieve the desired mechanical properties. Annealing is typically done at temperatures between 704°C (1300°F) and 871°C (1600°F).

The following table lists only some of the grades:

Hunan Dinghan New Material Technology Co., LTD