436L / 1.4371 Stainless Steel Strip ASTM A240 SS Coil From TISCO

436L stainless steel is a low-carbon ferritic stainless steel, containing about 17% chromium and a small amount of molybdenum (Mo), with excellent corrosion resistance, oxidation resistance and high temperature resistance. Compared with 409L, 436L has a higher chromium content and the addition of molybdenum, which further improves its performance in corrosive environments, especially in chlorine-containing environments such as salt water, pitting and crevices corrosion resistance. 436L stainless steel belt is widely used in automotive, home appliances, construction and chemical industry and other fields.

Chemical composition (%) of 436L Stainless Steel Strip

• Element content range
• Carbon (C) ≤0.025
• Silicon (Si) ≤1.00
• Manganese (Mn) ≤1.00
• Phosphorus (P) ≤0.040
• Sulfur (S) ≤0.030
• Chromium (Cr) 16.00-18.00
• Molybdenum (Mo) 0.75-1.25
• Titanium (Ti) 0.10-0.60

Physical property of 436L Stainless Steel Strips

• Density: 7.75 g/cm³
• Melting point: 1425-1510°C
• Thermal expansion coefficient: 10.4 ×10^-6 /K (20-100°C)
• Thermal conductivity: 25.1 W/m·K (100°C)
• Specific heat capacity: 460 J/kg·K (20°C)

Mechanical property of 436L Stainless Steel Strip

• Tensile strength: ≥450 MPa
• Yield strength: ≥250 MPa
• Elongation: ≥20%
• Hardness: ≤200 HV

Performance characteristics

• Corrosion resistance: The high chromium content and the addition of molybdenum give it excellent resistance to pitting and crevice corrosion in chlorine-containing environments such as salt water.
• Oxidation resistance: It can still maintain good antioxidant properties under high temperature environment.
• Welding performance: Low carbon design makes it excellent welding performance, no heat treatment after welding.
• Processing performance: easy cold processing and forming, suitable for manufacturing complex shape parts.
• High temperature resistance: suitable for high temperature environment, such as automobile exhaust system.

The production and inspection of 436L stainless steel belts usually follow the following international or industry standards:

• ASTM A240: Standard for Pressure Vessels and Universal Stainless Steel sheets, sheets, and strips.
• JIS G4305: Japanese Standard for cold-rolled stainless steel sheets and strips.
• EN 10088-2: European Standard for corrosion-resistant steel sheets and strips for general use in stainless steel.
• GB/T 3280: China stainless steel cold-rolled steel sheet and strip standard.

Specification

• The common specifications of 436L stainless steel belt are as follows:
• Thickness: 0.6mm-3.0mm
• Width: 10mm-1250mm
• Length: Can be customized according to requirements, usually in roll or plate shape
• Surface state: 2D

Application field
Automotive industry:

• Exhaust system (exhaust pipe, muffler)
• Catalytic converter
• Fuel tank

Home appliance Industry:

• Washing machine barrel
• Microwave case
• Water heater liner

Construction industry:

• Roof and wall decoration materials
• Structural support

Chemical Industry:

• Corrosion resistant vessel
• Pipes and tanks

Food processing Industry:

• Food processing equipment
• Conveyor belt

Other areas:

• Heat exchanger
• Boiler component
• Agricultural equipment

436L stainless steel tape with its excellent corrosion resistance, oxidation resistance, welding performance and processing performance, widely used in automotive, home appliances, construction, chemical and food processing and other fields. Its high chromium content and the addition of molybdenum make it particularly outstanding in chlorine-containing environments, and it is a high-performance stainless steel material.