| Sign In | Join Free | My benadorassociates.com |
|
| Categories | Ink Additives |
|---|---|
| Brand Name: | DR |
| Model Number: | DR-262 |
| Certification: | SGS |
| Place of Origin: | Made in China |
| MOQ: | 500kgs |
| Price: | price negotiation |
| Payment Terms: | L/C,D/A,D/P,T/T,Western Union |
| Supply Ability: | 500mts/month |
| Delivery Time: | about 15 working days |
| Packaging Details: | 10kg/bag |
| Product name: | Hydrophilic Fumed Silica DR-262 |
| Appearance: | White powder |
| CAS NO.: | 7631-86-9 |
| Application: | Powder coating industries |
| Feature: | Good thickening |
| Specific Surface Area(BET),m²/g: | 110±30 |
| pH (4% suspension,water to methanol ratio 1:1): | 4.0-7.0 |
| Silica content(based on ignited material): | ≥99.8% |
| Carbon content: | 4.0-7.0% |
| Loss on drying*1 (105℃,2h): | ≤0.7% |
| Company Info. |
| ANHUI DERUN IMPORT & EXPORT TRADING CO., LTD |
| Verified Supplier |
| View Contact Details |
| Product List |
Good Stability Hydrophilic Fumed Silica For Silicone Rubber
Hydrophilic fumed silica DR-262 has good thickening&thixotropy properties,and stability in epoxy resin system products,high loading enables it great reinforce performance for polymers.
Specification of matting agent
| Appearance | White Powder |
| Silica content (based on ignited material),% | ≥99.8 |
Specific Surface Area(BET),m²/g | 110±30 |
pH (4% suspension,water to methanol ratio 1:1) | 4.0-7.0 |
Loss on drying*1 (105℃,2h) | ≤0.7% |
Loss on ignition*2 | ≤10% |
Tamped density*2 | 45-70 g/l |
Carbon conten | 4.0-7.0% |
Note:*1 represents test conditions of 105℃,2h,data represents ex
plant value;
*2 represents the product based on 105℃,2h;the test standard refers to GB/T 20020.
Packing of matting agent
Matting agent are packed in multi-layered kraft paper bags of 10kg/bag or polypropylene bags of 150kg/bag.
Storage of matting agent
It is recommended that the product be stored in a dry,cool environment and avoid contact with volatile substances.It should be used within two years from the date of production.


|
|