| Brand Name: | RONGSHENG |
| Certification: | ISO9001 |
| Place of Origin: | Henan, China |
| Raw Material: | Corundum And Mullite |
| Customized: | yes |
| Installation Method: | Vibration Casting |
| Rupture Strength: | ≥6Mpa at 1100℃×3h |
| Usage: | Furnace Liner,working lining casting |
| Flexural Strength: | 1d ≥6.0MPa |
| Refractoriness: | Above 1700°C |
| Product: | Acid-Resistant Castable |
| Working Temperature: | 1800℃ |
| Compressivestrength: | ≥ 50 MPa (after 3 days curing) |
| Application: | coke oven |
| Applicationtemperature: | Up to 1800°C |
| Type: | manufacture |
| Made: | Henan |
| Alumina Content: | 50% |
| Company Info. |
| Zhengzhou Rongsheng Refractory Co., Ltd. |
| Verified Supplier |
| View Contact Details |
| Product List |
Rongsheng Refractory Gunning Materials High Refractoriness Alumina Silicate Spray Coatings Induction Furnace Refractory Gunning Mix
Refractory Gunning Mix:
Gunning mix is composed of refractory aggregate, refractory powder, water, binder, mineralizer, plasticizer, and firing aid. It is a fire-resistant mixture constructed by spraying method.The materials of gunning mix include silicon aluminum, magnesium, corundum, and phosphate. It is also divided into lightweight,medium heavy weight and heavy weight gunning mix.
Light weight gunning mix is used for thermal insulation and insulation lining, medium heavy weight can be used as both thermal insulation and working lining for mediuContact Usm and low temperature furnaces, heavy weight gunning mix is mainly used as working lining.
Features and Advantages of Refractory Gunning Mix
refractory gunning mix has the characteristics of high adhesive rate,less resilience,high strength and easy gunning etc.scour resistance,impact resistance,erosion resistance.anti-scouring, wear resistance and excellent performances.
Application of Refractory Gunning Mix
Steel Industry,Energy Industry,Building Materials.It serves as a protective layer on the inner surface of blast furnace and hot blast furnace shells, as well as a working lining for blast furnace heads, coal gas outlet pipe, and dust collectors.
Refractory Material Gunning Mix Technique Data
| Item | Specification | |||
| LGP0.8 | LGP1.0 | LGP1.3 | ||
| Al2O3 % | ≥30 | ≥35 | ≥40 | |
| Bulk Density,g/cm3 110℃×24h | ≤0.8 | ≤1.0 | ≤1.3 | |
| CCS, MPa | 110℃×24h | ≥4 | ≥5 | ≥7 |
| Test Temperature, ×3h | ≥3 800℃ | ≥4 1000℃ | ≥5 1200℃ | |
| PLC, % Test Temperature, ×3h | ±0.8 800℃ | ±0.8 1000℃ | ±0.8 1200℃ | |
| Thermal Conductivity, W/(m·K) 350℃±25℃ | ≤0.21 | ≤0.25 | ≤0.35 | |
| Test Temperature, ℃ | 800 | 1000 | 1200 | |
| Item | Specification | |||
| LGP1.5 | LGP1.8 | LGP1.8T | ||
| Al2O3 % | ≥42 | ≥45 | ≥55 | |
| Bulk Density,g/cm3 110℃×24h | ≤1.5 | ≤1.8 | ≤1.8 | |
| CCS, MPa | 100℃×24h | ≥12 | ≥15 | ≥12 |
| Test Temperature, ×3h | ≥10 1300℃ | ≥13 1300℃ | ≥10 1400℃ | |
| PLC, % Test Temperature×3h | ±0.8 1300℃ | ±0.8 1300℃ | ±1.0 1400℃ | |
| Thermal Conductivity, W/(m·K) 350℃±25℃ | ≤0.4 | ≤0.7 | ≤0.75 | |
| Max Working Temperature, ℃ | 1300 | 1300 | 1500 | |
|
High Temperature Unshaped Refractories A600 Ca60 Ca80 High Alumina Refractory Cement For Furnace Construction
Furnace Kiln Oven Phosphate Bonded Unshape Refractory Material High Alumina Refractory Castable For Boiler
High Temperature Kiln Castable Refractory Cement Quick-Drying Explosion-Proof Castable
High Performance Low Cement Castable Refractory Mullite Castable For High Temperature Furnaces
Low Cement Castable Refractory Cement For Iron Making Furnace , Heat Resistant
High Strength Steel Fiber Refractory Castable Wear Resistance Performance
Gray color Corundum Powder Refractory Mortar Of Clay Bricks And High Alumina Brick
High Performance Glass Kiln Insulating Castable Refractory Of Thermal Equipments
High Strength Alkali Proof High Alumina Castable Refractory For Kiln Hood Lining
Fast Hard High Strength Castable Refractory Cement For Metallurgy And Petroleum Industry