Vacuum Oxygen Atmosphere Industrial Box Furnace 1700 Ordm C 25kW

Industrial 1700°C HBF52-17O temperature box furnace designed for high-temperature applications with dimensions of 1150×1970×1300mm (W×H×D).

Primarily used for:

• Zirconia ceramics processing
• Alumina ceramics production
• Ferrites and magnetic materials manufacturing
• Electronic components fabrication
• Ceramic filters in high temperature binder burn off and sintering processes

• Rated Temperature: 1650°C
• Maximum Temperature: 1700°C
• Effective Dimensions: 350 × 300 × 500mm (W×H×D)
• Heating Method: U-shaped MoSi2 Heating Elements
• Process Atmosphere: Air/Oxygen
• Temperature Control Stability: ±1°C with PID parameter self-tuning
• Temperature Uniformity: Better than ±5°C (after 2 hours insulation at 1650°C)
• Thermocouple: B Type
• Temperature Control Points: 1
• Temperature Measurement Points: 1
• Temperature Profiles: 4×16 steps
• Exhaust System: One exhaust port with automatic cover
• Alarm System: Sound and light alarms for over temperature, thermocouple failure
• Maximum Heating Power: 25kW
• Insulation Power: ≤ 10kW
• Heating Speed: RT~1200°C ≤5°C/min, 1200~1700°C ≤2°C/min
• Surface Temperature Rise: ≤ 35°C
• Weight: Approximately 900kg
• Furnace Dimensions: Approximately 1620×1960×1220mm (W×H×D)
• Appearance Color: Light gray

• Environmental conditions: Temperature 0-40°C, humidity ≤80% RH, no corrosive gas, no strong airflow disturbance
• Process air conditions: Clean, dry, oil-free compressed air, pressure 0.2-0.4Mpa, gas consumption 2-6m³/h
• Ventilation system: Non-contact access to user pumping system with capacity >10m³/h
• Ground requirements: Level surface, no significant vibration, bearing capacity >300Kg/m²
• Power conditions: Capacity >34kVA, 3 phases 5 lines, voltage 220/380V, frequency 50Hz
• Installation site: Minimum 2000×3000×1500mm (W×H×D) with area >3m²