| Sign In | Join Free | My benadorassociates.com |
|
| Categories | Tungsten Carbide Seal Ring |
|---|---|
| Place of Origin: | China |
| MOQ: | 5 |
| Price: | $15-68 |
| Material Composition: | Tungsten carbide and cobalt |
| Alloy Specification: | YG8, YG6, YG6X, YG9C, YG11C, YG13C |
| Shape: | Cylindrical |
| Surface Finish: | Glossy |
| Color: | Black Alloy |
| Density Range: | 12.33-15.0 g/cm³ |
| Hardness Range: | 86.5-93.6 HRA |
| TRS Range: | 1800-3800 Mpa |
| Porosity Grade: | A02/B00/C00 |
| Grain Size: | 0.4-2.4 μm |
| WC Content: | 69.2-94.0% |
| Ni Content: | 6.0-16.0% |
| Ti Content: | 0-7.4% |
| TaC Content: | 0-13.8% |
| Customization: | Available per customer drawing or sample |
| Company Info. |
| Chengdu Kedel Technology Co.,Ltd |
| Verified Supplier |
| View Contact Details |
| Product List |
Grade | Composition(% in weight) | Physical Properties | |||||||||||||
Densityg/cm³(±0.1) | HardnessHRA(±0.5) | TRS Mpa(min) | Porosity | ||||||||||||
WC | Ni | Ti | TaC | A/B/C | |||||||||||
KD115/YG6X | 93.5 | 6.0 | - | 0.5 | 14.90 | 93.0 | 2700 | A02/B00/C00 | 0.6-0.8 | ||||||
KD335/YG10X | 89.0 | 10.5 | - | 0.5 | 14.40 | 91.8 | 3800 | A02/B00/C00 | 0.6-0.8 | ||||||
KG6/YG6 | 94.0 | 6.0 | - | - | 14.90 | 90.5 | 2500 | A02/B00/C00 | 1.2-1.6 | ||||||
KG8/YG8 | 92.0 | 8.0 | - | - | 14.75 | 90.0 | 3200 | A02/B00/C00 | 1.2-1.6 | ||||||
KG9/YG9 | 91.0 | 9.0 | - | - | 14.60 | 89.0 | 3200 | A02/B00/C00 | 1.2-1.6 | ||||||
KG9C/YG9C | 91.0 | 9.0 | - | - | 14.60 | 88.0 | 3200 | A02/B00/C00 | 1.6-2.4 | ||||||
KG10/KG10 | 90.0 | 10.0 | - | - | 14.50 | 88.5 | 3200 | A02/B00/C00 | 1.2-1.6 | ||||||
KG11/YG11 | 89.0 | 11.0 | - | - | 14.35 | 89.0 | 3200 | A02/B00/C00 | 1.2-1.6 | ||||||
KG11C/YG11C | 89.0 | 11.0 | - | - | 14.40 | 87.5 | 3000 | A02/B00/C00 | 1.6-2.4 | ||||||
KG13/YG13 | 87.0 | 13.0 | - | - | 14.20 | 88.7 | 3500 | A02/B00/C00 | 1.2-1.6 | ||||||
KG13C/YG13C | 87.0 | 16.0 | - | - | 14.20 | 87.0 | 3500 | A02/B00/C00 | 1.6-2.4 | ||||||
KG15/YG15 | 85.0 | 15.0 | - | - | 14.10 | 87.5 | 3500 | A02/B00/C00 | 1.2-1.6 | ||||||
KG15C/YG15C | 85.0 | 15.0 | - | - | 14.00 | 86.5 | 3500 | A02/B00/C00 | 1.6-2.4 | ||||||
KD118/YG8X | 91.5 | 8.5 | - | - | 14.50 | 93.6 | 3800 | A02/B00/C00 | 0.4-0.6 | ||||||
KD338/YG12X | 88.0 | 12.0 | - | - | 14.10 | 92.8 | 2200 | A02/B00/C00 | 0.4-0.6 | ||||||
KD25/P25 | 77.4 | 8.5 | 6.5 | 6.0 | 12.60 | 91.8 | 2200 | A02/B00/C00 | 1.0-1.6 | ||||||
KD35/P35 | 69.2 | 10.5 | 5.2 | 13.8 | 12.70 | 91.1 | 2500 | A02/B00/C00 | 1.0-1.6 | ||||||
KD10/M10 | 83.4 | 7.0 | 4.5 | 4.0 | 13.25 | 93.0 | 2000 | A02/B00/C00 | 0.8-1.2 | ||||||
KD20/M20 | 79.0 | 8.0 | 7.4 | 3.8 | 12.33 | 92.1 | 2200 | A02/B00/C00 | 0.8-1.2 | ||||||
Grade | Composition(% in weight) | Physical Properties | Equivalen to domestic | |||||||||||
Densityg/cm³(±0.1) | HardnessHRA(±0.5) | TRS Mpa(min) | Porosity ABC | Grain size(μm) | ||||||||||
WC | Ni | Ti | ||||||||||||
KDN6 | 93.8 | 6.0 | 0.2 | 14.6-15.0 | 89.5-90.5 | 1800 | A02B00C00 | 0.8-2.0 | YN6 | |||||
KDN7 | 92.8 | 7.0 | 0.2 | 14.4-14.8 | 89.0-90.0 | 1900 | 0.8-1.6 | YN7 | ||||||
KDN8 | 91.8 | 8.0 | 0.2 | 14.5-14.8 | 89.0-90.0 | 2200 | 0.8-2.0 | YN8 | ||||||
KDN12 | 87.8 | 12.0 | 0.2 | 14.0-14.4 | 87.5-88.5 | 2600 | 0.8-2.0 | YN12 | ||||||
KDN15 | 84.8 | 15.0 | 0.2 | 13.7-14.2 | 86.5-88.0 | 2800 | 0.6-1.5 | YN15 | ||||||
|