| Material: | 100% pure tungsten carbide powder | 
| Surface: | Glossy | 
| Shape: | Circle | 
| Color: | Black | 
| Grade: | YG8/YG9C/YG11C | 
| Density: | 14.90 g/cm³ (YG6X) | 
| Hardness: | 93.0 HRA (YG6X) | 
| TRS: | 2700 Mpa (YG6X) | 
| Porosity: | A02/B00/C00 (YG6X) | 
| Grain size: | 0.6-0.8 μm (YG6X) | 
| WC Composition: | 93.5% (YG6X) | 
| Ni Composition: | 6.0% (YG6X) | 
| TaC Composition: | 0.5% (YG6X) | 
| Minimum TRS: | 1800 Mpa (KDN6) | 
| Maximum TRS: | 3800 Mpa (YG8X) | 
| Company Info. | 
| Chengdu Kedel Technology Co.,Ltd | 
| Verified Supplier | 
| View Contact Details | 
| Product List | 
Grade  | Composition(% in weight)  | Physical Properties  | |||||||||||||
Densityg/cm³(±0.1)  | HardnessHRA(±0.5)  | TRS Mpa(min)  | Porosity  | ||||||||||||
WC  | Ni  | Ti  | TaC  | A/B/C  | |||||||||||
KD115/YG6X  | 93.5  | 6.0  | -  | 0.5  | 14.90  | 93.0  | 2700  | A02/B00/C00  | 0.6-0.8  | ||||||
KD335/YG10X  | 89.0  | 10.5  | -  | 0.5  | 14.40  | 91.8  | 3800  | A02/B00/C00  | 0.6-0.8  | ||||||
KG6/YG6  | 94.0  | 6.0  | -  | -  | 14.90  | 90.5  | 2500  | A02/B00/C00  | 1.2-1.6  | ||||||
KG8/YG8  | 92.0  | 8.0  | -  | -  | 14.75  | 90.0  | 3200  | A02/B00/C00  | 1.2-1.6  | ||||||
KG9/YG9  | 91.0  | 9.0  | -  | -  | 14.60  | 89.0  | 3200  | A02/B00/C00  | 1.2-1.6  | ||||||
KG9C/YG9C  | 91.0  | 9.0  | -  | -  | 14.60  | 88.0  | 3200  | A02/B00/C00  | 1.6-2.4  | ||||||
KG10/KG10  | 90.0  | 10.0  | -  | -  | 14.50  | 88.5  | 3200  | A02/B00/C00  | 1.2-1.6  | ||||||
KG11/YG11  | 89.0  | 11.0  | -  | -  | 14.35  | 89.0  | 3200  | A02/B00/C00  | 1.2-1.6  | ||||||
KG11C/YG11C  | 89.0  | 11.0  | -  | -  | 14.40  | 87.5  | 3000  | A02/B00/C00  | 1.6-2.4  | ||||||
KG13/YG13  | 87.0  | 13.0  | -  | -  | 14.20  | 88.7  | 3500  | A02/B00/C00  | 1.2-1.6  | ||||||
KG13C/YG13C  | 87.0  | 16.0  | -  | -  | 14.20  | 87.0  | 3500  | A02/B00/C00  | 1.6-2.4  | ||||||
KG15/YG15  | 85.0  | 15.0  | -  | -  | 14.10  | 87.5  | 3500  | A02/B00/C00  | 1.2-1.6  | ||||||
KG15C/YG15C  | 85.0  | 15.0  | -  | -  | 14.00  | 86.5  | 3500  | A02/B00/C00  | 1.6-2.4  | ||||||
KD118/YG8X  | 91.5  | 8.5  | -  | -  | 14.50  | 93.6  | 3800  | A02/B00/C00  | 0.4-0.6  | ||||||
KD338/YG12X  | 88.0  | 12.0  | -  | -  | 14.10  | 92.8  | 2200  | A02/B00/C00  | 0.4-0.6  | ||||||
KD25/P25  | 77.4  | 8.5  | 6.5  | 6.0  | 12.60  | 91.8  | 2200  | A02/B00/C00  | 1.0-1.6  | ||||||
KD35/P35  | 69.2  | 10.5  | 5.2  | 13.8  | 12.70  | 91.1  | 2500  | A02/B00/C00  | 1.0-1.6  | ||||||
KD10/M10  | 83.4  | 7.0  | 4.5  | 4.0  | 13.25  | 93.0  | 2000  | A02/B00/C00  | 0.8-1.2  | ||||||
KD20/M20  | 79.0  | 8.0  | 7.4  | 3.8  | 12.33  | 92.1  | 2200  | A02/B00/C00  | 0.8-1.2  | ||||||
Grade  | Composition(% in weight)  | Physical Properties  | Equivalen to domestic  | |||||||||||
Densityg/cm³(±0.1)  | HardnessHRA(±0.5)  | TRS Mpa(min)  | Porosity ABC  | Grain size(μm)  | ||||||||||
WC  | Ni  | Ti  | ||||||||||||
KDN6  | 93.8  | 6.0  | 0.2  | 14.6-15.0  | 89.5-90.5  | 1800  | A02B00C00  | 0.8-2.0  | YN6  | |||||
KDN7  | 92.8  | 7.0  | 0.2  | 14.4-14.8  | 89.0-90.0  | 1900  | 0.8-1.6  | YN7  | ||||||
KDN8  | 91.8  | 8.0  | 0.2  | 14.5-14.8  | 89.0-90.0  | 2200  | 0.8-2.0  | YN8  | ||||||
KDN12  | 87.8  | 12.0  | 0.2  | 14.0-14.4  | 87.5-88.5  | 2600  | 0.8-2.0  | YN12  | ||||||
KDN15  | 84.8  | 15.0  | 0.2  | 13.7-14.2  | 86.5-88.0  | 2800  | 0.6-1.5  | YN15  | ||||||
                                 
                             |